#DISTRIBUTEDBY=Aerosol Refractive Index Archive (www.atm.ox.ac.uk/project/RI/) #DESCRIPTION=Refractive indices of Andesite. #SUBSTANCE=Andesite #SAMPLEFORM=Solid #TEMPERATURE= #CONCENTRATION= #DOI=10.1016/0019-1035(73)90115-2 #REFERENCE=J. B. Pollack, O. B. Toon, and B. N. Khare, Icarus 19, 372-389 (1973). #CONTACT= #COMMENT=From the original paper, missing values were interpollated. #FORMAT=WAVL N K 0.21 1.6 NaN 0.23 1.56 NaN 0.25 1.53 NaN 0.27 1.5 NaN 0.29 1.48 NaN 0.3 1.47 0.00091 0.32 1.47 0.00099 0.34 1.47 0.001 0.36 1.47 0.0011 0.38 1.47 0.0011 0.4 1.47 0.0012 0.42 1.47 0.0012 0.44 1.47 0.0013 0.46 1.47 0.0013 0.48 1.47 0.0013 0.5 1.47 0.0014 0.52 1.47 0.0014 0.54 1.47 0.0014 0.56 1.47 0.0015 0.58 1.47 0.0015 0.6 1.47 0.0015 0.7 1.47 0.0017 0.8 1.47 0.0019 0.9 1.47 0.0021 1 1.47 0.0023 1.1 1.47 0.0025 1.2 1.47 0.0027 1.3 1.47 0.0029 1.4 1.47 0.003 1.5 1.47 0.0032 1.6 1.469 0.0033 1.7 1.4665 0.0034 1.8 1.4635 0.0035 1.9 1.461 0.0036 2 1.46 0.0038 2.1 1.46 0.0038 2.2 1.46 0.0039 2.3 1.46 0.004 2.4 1.46 0.0041 2.5 1.46 0.0041 2.55 1.46 0.0042 2.6 1.46 0.0042 2.65 1.46 0.0044 2.7 1.46 0.0045 2.75 1.46 0.005 2.8 1.46 0.0053 2.85 1.46 0.0054 2.9 1.46 0.0056 2.95 1.46 0.0056 3 1.46 0.0056 3.05 1.4599 0.0055 3.1 1.4594 0.0055 3.15 1.4588 0.0055 3.2 1.4578 0.0054 3.25 1.4567 0.0055 3.3 1.4554 0.0056 3.35 1.4539 0.0056 3.4 1.4523 0.0056 3.45 1.4506 0.0057 3.5 1.4488 0.0058 3.6 1.4449 0.006 3.7 1.4409 0.006 3.8 1.437 0.0061 3.9 1.4333 0.0061 4 1.43 0.0063 4.25 1.4229 0.0068 4.5 1.4159 0.0073 4.75 1.4086 0.0078 5 1.4 0.0086 5.25 1.3899 0.0094 5.5 1.3782 0.01 5.75 1.3649 0.011 6 1.35 0.012 6.5 1.31 0.017 7 1.26 0.028 7.5 1.18 0.049 8 1.06 0.1 8.25 0.97 0.16 8.5 0.87 0.27 8.75 0.78 0.48 9 0.77 0.85 9.5 1.31 0.92 10 1.6 1.1 10.5 1.93 0.86 11 2.16 0.42 11.5 1.96 0.2 12 1.83 0.13 12.5 1.74 0.1 13 1.67 0.095 13.5 1.6 0.096 14 1.54 0.11 14.5 1.47 0.13 15 1.4 0.17 15.5 1.32 0.26 16 1.28 0.41 16.5 1.38 0.58 17 1.54 0.59 17.5 1.57 0.54 18 1.59 0.58 18.5 1.68 0.62 19 1.78 0.56 19.5 1.79 0.47 20 1.76 0.42 20.5 1.71 0.4 21 1.66 0.42 21.5 1.63 0.47 22 1.62 0.53 22.5 1.65 0.6 23 1.7 0.66 23.5 1.77 0.69 24 1.84 0.69 25 1.94 0.65 26 2.01 0.66 27 2.1 0.53 28 2.08 0.48 29 2.08 0.47 30 2.11 0.47 35 2.21 0.27 40 2.16 0.15 45 2.11 0.097 50 2.08 0.073